杨荣博士在Macromolecules上发表研究论文

   发布时间: 2017-04-14    访问次数: 166

题目:

Chain Folding in Main-Chain Liquid Crystalline Polyester with Strong π–π Interaction: An Efficient β-Nucleating Agent for Isotactic Polypropylene

作者:

Rong Yang*, Lv Ding, Weilong Chen, Li Chen, Xin Zhang, and Jinchun Li*

单位:

Jiangsu Key Laboratory of Environmentally Friendly Polymeric Materials, School of Materials Science and Engineering, Jiangsu Collaborative Innovation Center of Photovolatic Science and Engineering, Changzhou University, Changzhou 213164, China

Center for Degradable and Flame-Retardant Polymeric Materials, College of Chemistry, National Engineering Laboratory of Eco-Friendly Polymeric Materials (Sichuan), Sichuan University, Chengdu 610064, China

出处: Macromolecules, 2017, 50 (4), pp 1610–1617

摘要:

The influence of the main-chain liquid crystalline polyester (PBDPS) on the crystallization and melting behaviors of isotactic polypropylene (iPP) has been investigated by differential scanning calorimetry (DSC), X-ray diffraction (WAXD), and polarized optical microscopy (POM). The results suggested that PBDPS is an efficient β-nucleating agent for iPP. The melting crystallization temperature as well as β-crystal of iPP increased with increasing of PBDPS content. The relative content of β-iPP crystals (kβ) can reach 96.6% while adding 4% PBDPS during isothermal crystallization at 135 °C. The increased β-nucleation efficiency was ascribed to the adjacent phenyl rings in side groups of PBDPS stacked well together even when the temperature was higher than its clearing point (Ti). Moreover, the distance between stacked phenyls is 0.32 nm, which is half of the unit cell parameter in the c-direction of β-iPP, indicating a lattice match between β-iPP and PBDPS.